The results of a study of heavy implantation of a LiNbO3 crystal with iron ions are reported for the first time. The X-cut LiNbO3 substrate was implanted with 40-keV Fe+ ions to the fluence of ...1.5·1017 ions/cm2. The sample reveals pronounced ferromagnetic properties at room temperature. However, the ferromagnetic response observed in the iron-implanted LiNbO3 differs from the magnetic behavior of other oxides implanted with iron ions under the same conditions. This difference occurs from the unusual magnetic phase composition of the implanted surface layer of the LiNbO3 in which the iron implant precipitates in the form of the nanoscale alloy of metallic iron with niobium. Based on Mössbauer spectroscopy data, we estimated the Nb content in the ion-synthesized nanosized alloy as ~12 at.%, which is much higher than the solid solubility limit of Nb in bulk Fe.
The results of a study of heavy implantation of a LiNbOsub.3 crystal with iron ions are reported for the first time. The X-cut LiNbOsub.3 substrate was implanted with 40-keV Fesup.+ ions to the ...fluence of 1.5·10sup.17 ions/cmsup.2 . The sample reveals pronounced ferromagnetic properties at room temperature. However, the ferromagnetic response observed in the iron-implanted LiNbOsub.3 differs from the magnetic behavior of other oxides implanted with iron ions under the same conditions. This difference occurs from the unusual magnetic phase composition of the implanted surface layer of the LiNbOsub.3 in which the iron implant precipitates in the form of the nanoscale alloy of metallic iron with niobium. Based on Mössbauer spectroscopy data, we estimated the Nb content in the ion-synthesized nanosized alloy as ~12 at.%, which is much higher than the solid solubility limit of Nb in bulk Fe.