Microstructure and ductility of Fe28Cr16Co alloy with additions of silicon, molybdenum, titanium and aluminiumVodopivec, Franc, 1931-2021 ...The microstructure of several alloys with base composition Fe28Cr16Co and addition up to 1.5% silicon, 0.32% titanium, 2.34% molybdenum and 1% aluminium was investigated in the temperature range 500 ... to 1250°C bu optical microscopy, hardness measurements and dilatomery. Also, ductility and wirw drawing tests were carried out on some alloys. The addition of silicon, titanium, molybdenium or 0.13% Al does not prevent the formation of ▫$\gamma$▫phase up to the temperature 1250°C and the formation of phase ▫$\sigma$▫ in the temperature range 700 to approximately 1000°C. The addition of 1% Al prevents the formation of phase ▫$\sigma$▫ and shifts the temperature of formation of phase ▫$\gamma$▫ to 1158°C. The addition of different elements does not affect significantly the spinodal decomposition of phase ▫$\alpha$▫. At increased temperature an interval of sufficient ductility for deformation by wire drawing was established. The ductility was greatly improved if the microstructure consisted of small inclusions of phase ▫$\gamma$▫ in a matrix of phase ▫$\alpha$▫, probably because the deformation by twinning was hindered. However, insufficient magnetic properties were obtained also after 80% of deformation.Vir: Zeitschrift für Metallkunde : international journal of materials research. - ISSN 0044-3093 (Bd. 85, Heft. 3, 1994, str. 207-212)Vrsta gradiva - članek, sestavni delLeto - 1994Jezik - angleškiCOBISS.SI-ID - 17097221
Avtor
Vodopivec, Franc, 1931-2021 |
Breskvar, Bojan |
Torkar, Matjaž |
Žvokelj, J. |
Gnidovec, D. |
Rodič, A.
Teme
duktilnost |
vlečenje žice |
magnetne lastnosti |
spinodalni razpad |
FeCrCo
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: Zeitschrift für Metallkunde : international journal of materials research. - ISSN 0044-3093 (Bd. 85, Heft. 3, 1994, str. 207-212)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Vodopivec, Franc, 1931-2021 | 00142 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: