Mironyuk, Ivan; Mykytyn, Igor; Vasylyeva, Hanna
Fìzika ì hìmìâ tverdogo tìla (Online), 09/2022, Letnik: 23, Številka: 3Journal Article
The phase composition and morphology of boron-containing TiO2 nanoparticles obtained by the sol-gel method were investigated. The solution of titanium aqua complex Ti (OH2)63+‧3Cl- was used as a precursor. Borate acid Н3ВО3 (promoter of the formation of rutile) was used as a modified reagent. A single-phase rutile TiO2 was obtained at a concentration of borate acid in the reaction mixture, which causes the formation of a 0.5В-TiO2 sample. The particles of 0.5В-TiO2 samples were in the villi-form, with a diameter of 0.8-1.2 nm, and a length of 16-24 nm. With an increase of the Н3ВО3 concentration in the reaction mixture, synthesized oxide materials (samples of 1.0В-TiO2 and 1.5В-TiO2) contain 70 % and 57% of anatase respectively, in addition to rutile phase. Titanium-borate monodentate molecules Ti(OH)3OB(OH)2‧2Н2О were formed during the synthesis of the 0.5B-TiO2 rutile sample. The interatomic distance of Ti-O in these particles is commensurate with the average length of the Ti-O – bond of TiO6 rutile octahedra. During the polycondensation process, the distance of the Ti-O molecule-promoter was reproduced as a pattern in the following octahedra of rutile crystals. Two types of titanium-borate molecules are formed in the reaction medium, during the synthesis of 1.0В-TiO2 and 1.5В-TiO2 samples. Molecules with a bidentate mononuclear structure Ті(ОН)2О2ВОН‧2Н2О in which the interatomic distance of Ti-O is commensurate with the average length of the Ti-O –bond in the anatase octahedra was formed. Therefore, titanium-borate molecules of the second type act as a promoter of the formation of the TiO2 anatase phase.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.