YOUNG, K; OUCHI, T; HUANG, B
Journal of power sources, 02/2014, Letnik: 248Journal Article
Annealing Nd-only AB3.74 metal hydride alloy was found to effectively increase composition homogeneity, main A2B7 phase abundance, and both gaseous phase and electrochemical hydrogen storage capacities, as well as to facilitate activation, and improve battery high-rate performance, charge retention, and cycle life. As the phase abundance of the main A2B7 phase increases in the alloy with higher annealing temperatures, the general electrochemical performance improves. Extending the annealing period from 5 to 16 h further increases the A2B7 phase abundance, but deteriorates the high-rate dischargeability due to the reduction of AB5 catalytic phase.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.