Heidari, G.; Tavakoli, H.; Mousavi Khoie, S. M.
Journal of materials engineering and performance, 11/2010, Letnik: 19, Številka: 8Journal Article
Composite plating is a method through which the fine particles of metallic or non-metallic compounds are co-deposited in a plated layer to improve surface properties such as lubrication, wear resistance, and corrosion resistance. In this study, nano-sized SiC particles were co-deposited with nickel from sulfamat bath using pulsed and direct currents. Scanning electron microscopy, microhardness, wear, and corrosion tests were carried out to characterize the coating properties. The results showed that microhardness, wear resistance, and corrosion resistance of Ni-SiC composite coatings increased compared to those of Ni films.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.