Ctibor, P.; Píš, I.; Kotlan, J.; Pala, Z.; Khalakhan, I.; Štengl, V.; Homola, P.
Journal of thermal spray technology, 10/2013, Letnik: 22, Številka: 7Journal Article
Rutile TiO 2 and Eskolaite Cr 2 O 3 powders were mechanically mixed and fed into the plasma jet simultaneously. The influence of the ratio of components on behavior of the plasma-sprayed coatings was observed using two different compositions, both at two different feeding distances. The produced coatings were analyzed by XRD, SEM, XPS, and light microscopy. Electrical resistivity was measured at voltages from 1 to 100 V. Photocatalytic decomposition of butane on the coatings was studied using visible light together with a setup typically used for UV-light tests. For the coatings with high TiO 2 content, besides rutile, low anatase content was identified. The coatings with predominant Cr 2 O 3 exhibited lower porosity and higher hardness. All coatings are relatively efficient photocatalysts for butane decomposition. Moreover, they have good mechanical properties governed predominantly by Cr 2 O 3 content as the harder component. It was proven that the spray process led to obtaining of robust photocatalytically active coatings.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.