Li, Peng-Hui; Guo, Wei-Guo; Huang, Wei-Dong; Su, Yu; Lin, Xin; Yuan, Kang-Bo
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 10/2015, Letnik: 647Journal Article
To understand and evaluate the thermomechanical property of Ti–6Al–4V alloy prepared by the 3D laser deposition technology, an uniaxial compression test was performed on cylindrical samples using an electronic universal testing machine and enhanced Hopkinson technique, over the range of strain rate from 0.001/s to 5000/s, and at initial temperatures from the room temperature to 1173K. The microstructure of the undeformed and deformed samples was examined through optical microscopy and the use of scanning electron microscope (SEM). The experimental results show the followings: (1) the anisotropy of the mechanical property of this alloy is not significant despite the visible stratification at the exterior surfaces; (2) initial defects, such as the initial voids and lack of fusion, are found in the microstructure and in the crack surfaces of the deformed samples, and they are considered as a major source of crack initiation and propagation; (3) adiabatic shear bands and shearing can easily develop at all selected temperatures for samples under compression; (4) the yield and ultimate strengths of this laser-deposited Ti–6Al–4V alloy are both lower than those of the Ti–6Al–4V alloy prepared by forging and electron beam melting, whereas both of its strengths are higher than those of a conventional grade Ti–6Al–4V alloy at high strain rate only. In addition to compression tests we also conducted tensile loading tests on the laser-deposited alloy at both low and high strain rates (0.1/s and 1000/s). There is significant tension/compression asymmetry in the mechanical response under high-strain-rate loading. It was found that the quasi-static tensile fracturing exhibits typical composite fracture characteristic with quasi-cleavages and dimples, while the high-strain-rate fracturing is characterized by ductile fracture behavior.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.