Ye, Beilin; Wen, Tongqi; Huang, Kehan; Wang, Cai‐Zhuang; Chu, Yanhui
Journal of the American Ceramic Society, July 2019, Letnik: 102, Številka: 7Journal Article
The formation possibility of (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C high‐entropy ceramic (HHC‐1) was first analyzed by the first‐principles calculations, and then, it was successfully fabricated by hot‐pressing sintering technique at 2073 K under a pressure of 30 MPa. The first‐principles calculation results showed that the mixing enthalpy and mixing entropy of HHC‐1 were −0.869 ± 0.290 kJ/mol and 0.805R, respectively. The experimental results showed that the as‐prepared HHC‐1 not only had an interesting single rock‐salt crystal structure of metal carbides but also possessed high compositional uniformity from nanoscale to microscale. By taking advantage of these unique features, it exhibited extremely high nanohardness of 40.6 ± 0.6 GPa and elastic modulus in the range from 514 ± 10 to 522 ± 10 GPa and relatively high electrical resistivity of 91 ± 1.3 μΩ·cm, which could be due to the presence of solid solution effects.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.