Paidar, M.; Tahani, K.; Vaira Vignesh, R.; Ojo, O.O.; Ezatpour, H.R.; Moharrami, A.
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 07/2020, Letnik: 791Journal Article
This paper investigates the effect of dwell time and heat treatment on the modified friction stir clinched (MFSC) joint of AA2024-T3/AA6061-T6 Al alloys. The precipitation-hardening heat treatment method involves the combination of solution heat treatment (at 520 °C for 1 h) and aging (at 165 °C for 18 h) processes. The microstructure, failure load, hardness, and fracture behavior of the as-welded and heat-treated MFSC joints were investigated. TEM images show that re-precipitation of strengthening Al2CuMg and MgZn2 phases, dislocation density, and tangles are more pronounced in the heat-treated MFSC joint. A rise in dwell time increases the average grain sizes (1.39–6.65 μm), tensile-shear strength (101–133 MPa), and cross tension strength (59–88 MPa) of the MFSC welded 2024-T3/6061-T6 joints due to an upsurge in the in-process exposure time-induced heat input and inter-material flow. An increase in dwell time beyond 15 s is undesirable. It induces the formation of nugget cracks and micro-voids in the joints and an impaired joint failure load consequently ensues. Heat treatment processing further causes grain coarsening (2.48–9.15 μm) and improves the hardness (at the weld center), tensile-shear (146 MPa), and cross tension (102 MPa) failure strengths of the MFSC joints due to the re-precipitated strengthening phases.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.