Neto, J. F. M.; Naeem, M.; Costa, T. H. C.; Lima, L. L. F.; Sousa, R. R. M.; Feitor, M. C.; Libório, M. S.; Nascimento, R. M.
Journal of materials science, 04/2023, Letnik: 58, Številka: 16Journal Article
In this study, we introduced a modified cathodic cage plasma deposition (CCPD) system to synthesize a Ti–Nb–C–N-based composite coating on AISI-4340 steel. This composite coating is widely applied in orthopedic joint implants due to its effective bioactivity and wear resistance. In the existing CCPD system, a metallic cathodic cage of a specific material is used to deposit the coating of such material. Thus, it cannot be used to deposit the coating of a composite material. Here, we inserted composite material rings (80% TiO 2 + 10% Nb 2 O 5 + 10% graphite) on the lid of the cathodic cage, where the cathodic cage holds these rings and works as a counter electrode for plasma generation. The composite coating is synthesized in nitrogen plasma at various temperatures (300–400 °C) and various hydrogen contents (20, 50, and 80%). It is observed that the hardness of AISI-4340 steel (280 HV 0.25 ) can be increased up to 1430 HV 0.25 for coating deposited at 400 °C and 50% hydrogen, which is 5 times higher than the untreated sample. The XRD pattern shows that composite coating consists of TiN, Ti 2 N, NbN, NbC, and TiO 2 . The contents of oxide phase TiO 2 are reduced by adding hydrogen gas to the processing environment; thus, the nitride-based composite coating can be synthesized. The wear volume is significantly reduced by composite coating, specifically while using higher hydrogen contents and higher temperatures. This study shows that this modified CCPD system can improve the hardness and wear resistance by synthesizing this composite coating. In contrast with conventional techniques, separate metallic targets for each element in composite coating (titanium, niobium, and carbon targets) are not required, simple equipment, rough vacuum level are required, and high-processing efficiency are advantages of this system. Graphical abstract
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.