Kim, Yanghoo; Jo, Min-Gu; Park, Ju-Won; Park, Hyung-Ki; Han, Heung Nam
Scripta materialia, February 2018, Letnik: 144Journal Article
The elastocaloric effect and functional fatigue life of the polycrystalline Ni50Ti45.3V4.7 shape memory alloy have been studied. Temperature changes on rapid loading and unloading of a mechanically trained specimen were directly measured at different compressive stress levels. It was found that the maximum elastocaloric strength was accomplished at the stress corresponding to the end point of a transformation plateau. In the fatigue test, no significant degradation occurred in the elastocaloric cooling ability after 5000cyclic loadings. Compared to pure NiTi, the present alloy showed improved efficiency and endurance limit of the functional stability. Display omitted