Zappettini, A.; Mingzheng Zha; Marchini, L.; Calestani, D.; Mosca, R.; Gombia, E.; Zanotti, L.; Zanichelli, M.; Pavesi, M.; Auricchio, N.; Caroli, E.
IEEE transactions on nuclear science, 08/2009, Letnik: 56, Številka: 4Journal Article
Two-inch-diameter CdZnTe crystals doped with indium were grown by the boron oxide encapsulated vertical Bridgman technique. The crystals showed large single crystalline yield and low etch pit density. The background impurity content was dominated by boron in concentration lower than 1 ppm. High resistivity was obtained and a procedure for contact preparation was developed. The mobility-lifetime product of the material was determined by both X-ray irradiation and photocurrent spectroscopy. The X-ray detector prepared with this material showed good spectroscopic performance.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.