Yasuda, H.Y.; Yamaoka, K.; Oda, Y.; Umakoshi, Y.
Scripta materialia, 10/2008, Letnik: 59, Številka: 7Journal Article
Tension–compression asymmetry of pseudoelasticity in Fe–23.0at.%Al single crystals with the D0 3 structure was quantitatively examined by analyzing stress–strain response during tension–compression loading. The crystals demonstrated large pseudoelasticity associated with to-and-fro motion of 1/4〈1 1 1〉 superpartial dislocations dragging antiphase boundaries. Pseudoelasticity based on {1 0 1} slip showed little tension–compression asymmetry while an activation of {2 1 1} slip resulted in the asymmetry depending on the moving direction of 1/4〈1 1 1〉 superpartials with a screw character during loading and unloading.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.