Duan, Shengchao; Cho, Jinhyung; Lee, Minjoo; Mu, Wangzhong; Park, Joo Hyun
Journal of alloys and compounds, 04/2023, Letnik: 939Journal Article
The present study provides a benchmark of a sustainable solution utilizing ferroalloys to prepare ultra-clean CoCrFeMnNi high-entropy alloy (HEA). The designed CaO-MgO-Al2O3 slags saturated with CaAl2O4-MgAl2O4 (CA-MA, Slag A) and CaO-MgO (C-M, Slag M) were used to refine the HEA in Al2O3 and MgO refractory in an induction furnace under high-purity Ar atmosphere at 1773 K. The characteristics of non-metallic inclusions in the sampled HEA at different time intervals were quantitatively investigated. The results showed that three types of inclusions, i.e., sulfide (MnS), oxide, and complex type (oxide+sulfide), were found in the HEA regardless of refractory and slag types. The oxide inclusions such as MnAl2O4 and MgAl2O4 spinel particles can exist stably in the HEA melted in Al2O3 and MgO refractories with slag A and slag M, respectively. This fact is also confirmed not only by the electrolytic extraction method with elimination of the alloy matrix affection but also by the thermodynamic stability diagram for the HEA. For the structure of the complex inclusions, the core of oxide inclusions usually can act as the subsequent nucleation site for MnS since the precipitation temperature of the oxide inclusions (above the liquidus temperature of the HEA, TL ≅ 1623 K) is higher than that of MnS (below the solidus temperature of the HEA, TS ≅ 1573 K). The HEA melted in the MgO refractory with slag M had a higher cleanliness compared with that melted in the Al2O3 refractory with slag A, indicating that the MgO refractory with C-M saturated CaO-MgO-Al2O3 slag is suitable for producing an ultra-clean CoCrFeMnNi HEA prepared by the ferroalloys feedstock as the raw materials. Display omitted •Novel and low-cost procedure was developed for manufacturing ultra-clean HEA using commercial ferroalloys feedstock.•Two kinds of crucibles and designed slag compositions were used to compare the cleanliness of the produced HEA.•MgO crucible with the CaO-MgO-Al2O3 slag saturated with CaO-MgO is suitable for refining the HEA at 1773 K.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.