Miao, Jian-Ying; Hwang, Dennis W; Narasimhulu, Kuppala V; Lin, Ping-I; Chen, Yit-Tsong; Lin, Sheng-Hsien; Hwang, Lian-Pin
Carbon (New York), 2004, 2004-00-00, Letnik: 42, Številka: 4Journal Article
Carbon spheres with diameters between 400 and 2000 nm were synthesized in large quantities by catalytic chemical vapor deposition (CCVD) method using Kaolin supported transition metal salts (M=Fe, Co, Ni, etc.) as catalysts. The reaction conditions for the synthesis of carbon spheres in different sizes are described. The reactivity of the carbon spheres in various organic solvents is discussed. The as-synthesized carbon spheres are composed of unclosed graphene layers with the interlayer distances 0.33–0.35 nm. These carbon spheres have been characterized by SEM, TEM, HRTEM, XRD, Raman, ESR and SQUID magnetization techniques. From the ESR and SQUID the metallic nature of the carbon spheres is described.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.