Chen, S.; Hirota, N.; Okuda, M.; Takeguchi, M.; Kobayashi, H.; Hanagata, N.; Ikoma, T.
Acta biomaterialia, 02/2011, Letnik: 7, Številka: 2Journal Article
Tilapia fish-scale type I atelocollagen hydrogels with aligned fibril structures were fabricated under a strong magnetic field of 6 or 12 T using two different methods. In the first method, a solution of acid-soluble collagen was neutralized with phosphate buffer saline and maintained in the magnetic field at 28 °C for 3 h. Under these conditions fibrogenesis occurs, and a hydrogel is formed. The hydrogel was subsequently crosslinked with ethyl-dimethylcarbodiimide (EDC). In the second method, the hydrogels were formed as described above, but in the absence of an applied magnetic field. Only after being crosslinked with EDC were these gels exposed to the magnetic field (28 °C for 3 h). Both methods led to alignment of the collagen fibrils perpendicular to the magnetic direction, the extent of which depended on the duration of magnetic treatment. Even after EDC treatment, collagen fibrils can align, indicating that crosslinking has taken place within fibrils. Both sorts of aligned hydrogels exhibited similar rheological properties with higher storage and loss moduli than were observed with unoriented gels. The hydrogels treated at 6 T had the best rheological properties. The decrease in tangent angle phase delta indicated that the ratio of elasticity to viscosity was greater in the crosslinked than in the non-crosslinked hydrogels. Atomic force microscopy images showed that magnetic treatment had no effect on the nanostructure of collagen fibrils. Differential scanning calorimetry measurements indicated that collagen hydrogels with and without magnetic treatment had the same denaturation temperature, 48 °C, while EDC crosslinking increased the denaturation temperature to 62 °C.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.