The effect of texturing (co-extrusion using blowing agent) on the longevity of a geomembrane (GMB) when immersed in synthetic municipal solid waste leachate is investigated over a ∼3 year period. Based on data at four temperatures (40, 55, 75, and 85 °C), the time to antioxidant depletion of the textured portion of a 1.5 mm core thickness high-density polyethylene (HDPE) GMB is 40% (standard oxidative induction time) and 9% (high-pressure oxidative induction time) faster compared to the 1.5 mm smooth edge of the GMB. However, despite this, stress crack resistance results show that texturing may have no significant effect on the time to nominal failure for this GMB. It is also shown that HDPE GMBs made from nominally the same resin but from different production lots have different rates of stress crack resistance degradation and hence time to nominal failure; this should be considered both in landfill design and landfill construction quality assurance.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.