Feng, Kai; Shen, Yao; Sun, Hailin; Liu, Dongan; An, Quanzhang; Cai, Xun; Chu, Paul K.
International journal of hydrogen energy, 08/2009, Letnik: 34, Številka: 16Journal Article
Amorphous carbon (a-C) film about 3 μm in thickness is coated on 316L stainless steel by close field unbalanced magnetron sputter ion plating (CFUBMSIP). The AFM and Raman results reveal that the a-C coating is dense and compact with a small size of graphitic crystallite and large number of disordered band. Interfacial contact resistance (ICR) results show that the surface conductivity of the bare SS316L is significantly increased by the a-C coating, with values of 8.3–5.2 mΩ cm 2 under 120–210 N/cm 2. The corrosion potential ( E corr) shifts from about −0.3 V vs SCE to about 0.2 V vs SCE in both the simulated anode and cathode environments. The passivation current density is reduced from 11.26 to 3.56 μA/cm 2 with the aid of the a-C coating in the simulated cathode environment. The a-C coated SS316L is cathodically protected in the simulated anode environment thereby exhibiting a stable and lower current density compared to the uncoated one in the simulated anode environment as demonstrated by the potentiostatic results.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.